Degree of conversion of resin cements polymerized under different thicknesses of feldspathic porcelain

Aim The aim of this study is to evaluate the degree of conversion (DC) of resin cements polymerized under different thicknesses of feldspathic dental ceramic. Methods: Forty samples of RelyX ARC and RelyX Veneer resin cements were polymerized under Starlight feldspathic ceramic discs (DeguDent Gmbh) with 0.5 mm, 1.2 mm, 1.8 mm, and 2.4 mm in thickness. The control group was cured without the interposition of ceramic. The DC measurements were performed 10 minutes, 1 hour, and 24 hours after the light-activation in a Nexus 670 FTIR spectrophotometer. Data were analyzed by two-way repeated measure ANOVA and Fisher PLSD test. Results: The RelyX ARC showed higher DC for all ceramic thicknesses. There was significant decrease in DC related to an increase in ceramic thickness. For RelyX ARC, the values of DC obtained after 1 hour and 24 hours did not differ statistically between them, but they were higher than those analyzed after 10 minutes. For RelyX Veneer cement, there was gradual increase in the DC up to 24 hours. Conclusion: The higher the thicknesses of ceramic, the lower DC of the resin cement

Avaliação da alteração dimensional linear de silicones para inclusão laboratorial / Evaluation of linear dimensional alteration of laboratorial inclusion silicone

Foi propósito deste estudo avaliar a alteração dimensional linear de 6 silicones porcondensação indicados para inclusão de próteses em laboratório: Labor Mass, Perfil Lab, Silon IP,Vipi Sil, Zetalabor e Zetalabor Titanium. A partir de uma matriz metálica e seguindo a especificaçãonº 19 da ADA, Revisão ISO 4823, e as instruções dos fabricantes, foram obtidas 120 réplicas dos6 materiais (n = 20). Para a verificação da alteração dimensional linear, as réplicas foram avaliadaspor meio de um microscópio comparador, sendo a primeira leitura realizada imediatamenteapós a obtenção e a segunda depois de 60 minutos. Os dados obtidos foram transformados emporcentagem por meio de uma fórmula matemática e submetidos à análise de variância, sendoas médias comparadas pelo teste de Tukey. Houve diferença significativa entre as mensuraçõesrealizadas imediatamente e após 60 minutos, independente do material utilizado, e quando osmateriais foram analisados conjuntamente (p < 0,05), as maiores médias foram obtidas após60 minutos. Com relação à interação entre os fatores material e tempo, pôde-se observar que, nosdois períodos analisados não houve diferença estatisticamente significante entre os materiais e ogrupo controle (matriz metálica) quando analisados isoladamente (p > 0,05). Todos os materiaistestados apresentaram comportamento semelhante no que diz respeito à alteração dimensionallinear, independente do período analisado, as leituras tardias (após 60 minutos) apresentarammaiores alterações dimensionais.

The objective of this study was to evaluate the linear dimensional alteration of6 codensing silicone materials indicated for laboratorial denture inclusion, being: Labor Mass,Perfl Lab, Silon IP, Vipi Sil, Zetalabor and Zetalabor Titanium. The materials were measuredand handled according to manufacturer instructions, and, the 19th ADA especifications and the4823 ISO Review for elastomeric materials were used as guides of the realized exams. The readingswere made trough a comparison microscopic, the first, imediately after the samples been obtained,and the second after 60 minutes. 20 samples of each material were made, totalizing 120 replicas.The data was analysed by two way ANOVA and mean were compared by Tukey test. There was adifference between the measures taken imediately and after 60 minutes, independing the materialused and when they were analysed together (p < 0.05). Therefore the highest mean were obtainedafter 60 minutes. In relation to interaction between the factor material and time, it was observedthat in both analysed periods there was no significantly estatistic difference among the materialsand the control group (metallic matrix), when analysed alone/apart (p > 0.05). All tested materialspresented a similar behavior in respect of linear dimensional alteration, in both times studied, wherethe later readings (after 60 minutes) presented higher dimensional alterations.

Análise da movimentação dos dentes artificiais em próteses totais superiores. / Artificial teeth movement analysis in upper complete denture. Influence of polishing

O propósito desse estudo foi o de verificar a influência do polimento sobre a posição relativa dos dentes artificiais de próteses totais superiores, quando essas são confeccionadas com diferentes tipos de materiais ou associações, analisando para tanto à diferença entre as distâncias dos dentes pelo método de computação gráfica. Foram confeccionadas quarenta próteses totais superiores idênticas, sendo divididas em oito grupos de cinco espécimes cada de acordo com o tipo de resina (Vipi-wave e Onda-cryl), tipo de silicone para inclusão (Vipi-sil e Zetalabor) e tipo de polimento. As próteses foram polimerizadas em microondas, demarcadas e submetidas ao polimento químico e ao polimento mecânico. Em cada fase as próteses foram digitalizadas em scanner de mesa e suas imagens exportadas para o software AutoCad 2000 que possibilitou a mensuração dos segmentos entre os pontos previamente demarcados nos dentes. Os dados foram sub-metidos ao tratamento estatístico, e os resultados possibilitaram concluir que o polimento físico resultou em alterações significantemente superiores ao polimento químico quando os dados foram analisados independentemente do grupo estudado (p<0,05). O polimento das próteses resultou na grande maioria das amostras em uma recuperação gradual da contração de polimerização. Os grupos em que a resina de eleição foi a Vipi-wave (T1, T1’, T2 e T2’) apresentaram-se menos susceptível ao polimento químico que os grupos em que a resina foi a Onda-cryl (T3, T3’, T4 e T4’).